Grey Cast Iron Magnetic Sifa

Ulinganisho wa Iron ya Grey				Muundo mdogo (Visehemu vya Kiasi) ((())
Uchina (GB/T 9439)	ISO 185	ASTM A48/A48M	EN 1561	Muundo wa Matrix
HT100 (HT10-26)	100	Na.20 F11401	EN-GJL-100	Pearlite: 30-70％, flakes coarse; Ferrite: 30-70％; Binary Phosphorus Eutectic: ＜7％
HT150 (HT15-33)	150	Na.25A F11701	EN-GJL-150	Pearlite: 40-90％, flakes kati coarse; Ferrite: 10-60％; Binary Phosphorus Eutectic:＜7％
HT200 (HT20-40)	200	Na.30A F12101	EN-GJL-200	Pearlite: ＞95％, flakes za kati; Ferrite＜5％; Binary Phosphorus Eutectic (4)
HT250 (HT25-47)	250	No.35A F12401 No.40A F12801	EN-GJL-250	Pearlite: ＞98％ flakes nyembamba za kati; Binary Phosphorus Eutectic:＜2％
HT300 (HT30-54)	300	Na.45A F13301	EN-GJL-300	Pearlite: ＞98％ flakes nyembamba za kati; Binary Phosphorus Eutectic:＜2％
HT350 (HT35-61)	350	No.50A F13501	EN-GJL-350	Pearlite: ＞98％ flakes nyembamba za kati; Binary Phosphorus Eutectic:＜1％

 

Sifa za sumaku za chuma cha kijivu hutofautiana sana, kutoka kwa upenyezaji mdogo na nguvu ya juu ya kulazimisha hadi upenyezaji wa juu na nguvu ndogo ya kulazimisha. Mabadiliko haya hasa hutegemea muundo mdogo wa chuma cha kijivu. Kuongeza vipengele vya alloying ili kupata mali zinazohitajika za magnetic hupatikana kwa kubadilisha muundo wa chuma cha kutupwa kijivu.

Ferrite ina upenyezaji wa juu wa sumaku na upotezaji mdogo wa hysteresis; pearlite ni kinyume chake, ina upenyezaji mdogo wa sumaku na upotezaji mkubwa wa hysteresis. Pearlite huundwa kuwa ferrite kwa matibabu ya joto ya anneal, ambayo inaweza kuongeza upenyezaji wa sumaku kwa mara nne. Kuongeza nafaka za ferrite kunaweza kupunguza upotezaji wa hysteresis. Uwepo wa saruji utapunguza msongamano wa sumaku, upenyezaji na ubaki, huku ukiongeza upenyezaji na upotezaji wa hysteresis. Uwepo wa grafiti coarse itapunguza remanence. Mabadiliko kutoka kwa grafiti ya aina ya A (graphite yenye umbo la flake ambayo inasambazwa sawasawa bila mwelekeo) hadi grafiti ya aina ya D (graphite iliyojikunja laini na usambazaji usio wa mwelekeo kati ya dendrites) inaweza kuongeza kwa kiasi kikubwa uingizaji wa sumaku na nguvu ya kulazimisha. .

Kabla ya kufikia joto muhimu lisilo la sumaku, ongezeko la joto huongeza kwa kiasi kikubwa upenyezaji wa sumaku ya chuma cha kijivu. Sehemu ya Curie ya chuma safi ni joto la mpito la α-γ la 770°C. Wakati asilimia kubwa ya silikoni ni 5%, sehemu ya Curie itafikia 730°C. Joto la uhakika la Curie la saruji bila silicon ni 205-220°C.

Muundo wa matrix ya darasa la kawaida la chuma cha kutupwa kijivu ni pearlite, na upenyezaji wao wa juu ni kati ya 309-400 μH/m.

 

Sifa za Sumaku za Chuma cha Grey Cast
Kanuni ya Grey Iron	Muundo wa Kemikali (%)
	C	Si	Mn	S	P	Ni	Cr
A	3.12	2.22	0.67	0.067	0.13	＜0.03	0.04
B	3.30	2.04	0.52	0.065	1.03	0.34	0.25
C	3.34	0.83 - 0.91	0.20 - 0.33	0.021 - 0.038	0.025 - 0.048	0.04	＜0.02
Sifa za Sumaku		A		B		C
		Pearlite	Ferrite	Pearlite	Ferrite	Pearlite	Ferrite
Carbide Carbon w(%)		0.70	0.06	0.77	0.11	0.88	/
Remanence / T		0.413	0.435	0.492	0.439	0.5215	0.6185
Nguvu ya Kulazimisha / A•m-1		557	199	716	279	637	199
Kupoteza kwa Hysteresis / J•m-3•Hz-1 (B=1T)		2696	-696	2729	1193	2645	938
Nguvu ya Uga wa Sumaku / kA•m-1 (B=1T)		15.9	-5.9	8.7	8.0	6.2	4.4
Max. Upenyezaji wa Sumaku / μH•m-1		396	1960	353	955	400	1703
Nguvu ya Uga wa Sumaku wakati Max. Upenyezaji wa Sumaku / A•m-1		637	199	1035	318	1114	239
Upinzani / μΩ•m		0.73	0.71	0.77	0.75	0.42	0.37

 

Hapa katika zifuatazo ni mali ya mitambo ya chuma kijivu kutupwa:

Sifa za Mitambo za Chuma cha Grey Cast
Bidhaa kulingana na DIN EN 1561	Pima	Kitengo	EN-GJL-150	EN-GJL-200	EN-GJL-250	EN-GJL-300	EN-GJL-350
			EN-JL 1020	EN-JL 1030	EN-JL 1040	EN-JL 1050	EN-JL 1060
Nguvu ya Mkazo	Rm	MPA	150-250	200-300	250-350	300-400	350-450
0.1% Nguvu ya Mavuno	Rp0,1	MPA	98-165	130-195	165-228	195-260	228-285
Elongation Nguvu	A	%	0,3 - 0,8	0,3 - 0,8	0,3 - 0,8	0,3 - 0,8	0,3 - 0,8
Nguvu ya Kukandamiza	σdB	MPa	600	720	840	960	1080
0,1% Nguvu ya Kukandamiza	σd0,1	MPa	195	260	325	390	455
Nguvu ya Flexural	σbB	MPa	250	290	340	390	490
Schuifspanning	σaB	MPa	170	230	290	345	400
Mkazo wa Shear	TtB	MPa	170	230	290	345	400
Modules ya elasticity	E	GPA	78 - 103	88 - 113	103 - 118	108 - 137	123 - 143
Nambari ya Poisson	v	-	0,26	0,26	0,26	0,26	0,26
Ugumu wa Brinell		HB	160 - 190	180 - 220	190 - 230	200 - 240	210 - 250
Ductility	σbW	MPa	70	90	120	140	145
Mvutano na mabadiliko ya shinikizo	σzdW	MPa	40	50	60	75	85
Kuvunja Nguvu	Klc	N/mm3/2	320	400	480	560	650
Msongamano		g/cm3	7,10	7,15	7,20	7,25	7,30