Matibabu ya Joto ya Utoaji wa Chuma cha pua cha Austenitic

Muundo wa kama-kutupwa waaustenitic chuma cha puacastings ni austenite + carbide au austenite + ferrite. Matibabu ya joto yanaweza kuboresha upinzani wa kutu wa castings austenitic chuma cha pua.

 

Daraja Sawa la Chuma cha pua cha Austenitic
AISI	W-stoff	DIN	BS	SS	AFNOR	UNE / IHA	JIS	UNI
304	1.4301	X5 CrNi 18 9	304 S15	2332	Z 6 CN 18.09	F.3551	SUS 304	X5CrNi18 10
305	1.4303	X5 CrNi 18 12	305 S 19	-	Z 8 CN 18.12	-	SUS 305	X8CrNi19 10
303	1.4305	X12 CrNiS 18 8	303 S 21	2346	Z 10 CNF 18.09	F.3508	SUS 303	X10CrNiS 18 09
304L	1.4306	X2 CrNiS 18 9	304 S12	2352	Z 2 CN 18.10	F.3503	SUS 304L	X2CrNi18 11
301	1.4310	X12 CrNi 17 7	-	2331	Z 12 CN 17.07	F.3517	SUS 301	X12CrNi17 07
304	1.4350	X5 CrNi 18 9	304 S 31	2332	Z 6 CN 18.09	F.3551	SUS 304	X5CrNi18 10
304	1.4350	X5 CrNi 18 9	304 S 31	2333	Z 6 CN 18.09	F.3551	SUS 304	X5CrNi18 10
304LN	1.4311	X2 CrNiN 18 10	304 S62	2371	Z 2 CN 18.10	-	SUS 304 LN	-
316	1.4401	X5 CrNiMo 18 10	316 S16	2347	Z 6 CND 17.11	F.3543	SUS 316	X5CrNiMo17 12
316L	1.4404	-	316 S 12/13/14/22/24	2348	Z 2 CND 17.13		SUS316L	X2CrNiMo17 12
316LN	1.4429	X2 CrNiMoN 18 13	-	2375	Z 2 CND 17.13	-	SUS 316 LN	-
316L	1.4435	X2 CrNiMo 18 12	316 S 12/13/14/22/24	2353	Z 2 CND 17.13	-	SUS316L	X2CrNiMo17 12
316	1.4436	-	316 S 33	2343	Z 6 CND18-12-03	-	-	X8CrNiMo 17 13
317L	1.4438	X2 CrNiMo 18 16	317 S 12	2367	Z 2 CND 19.15	-	SUS 317 L	X2CrNiMo18 16
329	1.4460	X3 CrNiMoN 27 5 2	-	2324	Z5 CND 27.05.Az	F.3309	SUS 329 J1	-
321	1.4541	X10 CrNiTi 18 9	321 S12	2337	Z 6 CND 18.10	F.3553	SUS 321	X6CrNiTi18 11
347	1.4550	X10 CrNiNb 18 9	347 S17	2338	Z 6 CNNb 18.10	F.3552	SUS 347	X6CrNiNb18 11
316Ti	1.4571	X10 CrNiMoTi 18 10	320 S 17	2350	Z 6 CNDT 17.12	F.3535	-	X6CrNiMoTi 17 12
309	1.4828	X15 CrNiSi 20 12	309 S 24	-	Z 15 CNS 20.12	-	SUH 309	X16 CrNi 24 14
330	1.4864	X12 NiCrSi 36 16	-	-	Z 12 NCS 35.16	-	SUH 330	-

 

1. Suluhisho la Matibabu ya joto

Ufafanuzi wa jumla wa matibabu ya joto ya suluhisho ni: inapokanzwa kutupwa hadi 950 ° C - 1175 ° C na kuiweka katika maji, mafuta au hewa baada ya uhifadhi wa joto ili kufuta kabisa carbides katika chuma cha pua ili kupata muundo wa awamu moja. Uchaguzi wa joto la suluhisho hutegemea maudhui ya kaboni katika chuma cha kutupwa. Kadiri maudhui ya kaboni yalivyo juu, ndivyo joto la myeyusho gumu linavyohitajika.

Ili kupunguza tofauti ya joto kati ya uso wa akitoa chuma na msingi wakati wa mchakato wa joto, njia ya joto ya matibabu ya ufumbuzi wa chuma cha pua austenitic inapaswa kuwa preheated kwa joto la chini na kisha haraka joto kwa joto ufumbuzi. Wakati wa kushikilia unapaswa kuongezeka sawia kadiri unene wa ukuta wa utupaji unavyoongezeka.

Njia ya baridi kwa ajili ya matibabu ya ufumbuzi inaweza kuwa maji, mafuta au hewa, ambayo maji hutumiwa zaidi. Upoaji wa hewa unafaa tu kwa kuta za chuma zenye kuta nyembamba.

 

Specifications ya Suluhisho Imara Matibabu ya Cast Austenitic Chuma cha pua
Daraja nchini China	Daraja Sawa Abroard	Suluhisho Joto / ℃	Ugumu / HBW
ZG03Cr18Ni10	/	1050 - 1100	/
ZG0Cr18Ni9	/	1080 - 1130	/
ZG1Cr18Ni9	G-X15CrNi18 8 (Daraja la Kijerumani)	1050 - 1100	140 - 190
ZGCr18Ni9Ti		950 - 1050	125 - 180
ZGCr18Ni9Mo2Ti	X18H9M2 (Daraja la Kirusi)	1000 - 1050	140 - 190
ZG1Cr18Ni12Mo2Ti	X18H12M2 (Daraja la Kirusi)	1100 - 1150	/
ZGCr18Ni11B	X18H11B (Daraja la Kirusi)	1100 - 1150	/
ZG03Cr18Ni10	CF-3 (Daraja la Marekani)	1040 - 1120	/
ZG08Cr19Ni11Mo3	CF-3M (Daraja la Marekani)	1040 - 1120	150 - 170
ZG08Cr19Ni9	CF-8 (Daraja la Marekani)	1040 - 1120	140 - 156
ZG08Cr19Ni10Nb	CF-8C (Daraja la Marekani)	1065 - 1120 (Kuimarishwa kwa 870 - 900)	149
ZG07Cr19Ni10Mo3	CF-8M (Daraja la Marekani)	1065 - 1120	156 - 210
ZG16Cr19Ni10	CF-16F (Daraja la Marekani)	1095 - 1150	150
ZG2Cr19Ni9	CF-20 (Daraja la Marekani)	1095 - 1150	163
ZGCr19Ni11Mo4	CG-8M (Daraja la Marekani)	1040 - 1120	176
ZGCr24Ni13		1095 - 1150	190
ZG1Cr24Ni20Mo2Cu3		1100 - 1150	/
ZG2Cr15Ni20	CK-20 (Daraja la Marekani)	1095 - 1175	144
ZGCr20Ni29Mo3Cu3	CH-7M (Daraja la Marekani)	1120	130
ZG1Cr17Mn13N		1100	223 - 235
ZG1Cr17Mn13Mo2CuN		1100	/
ZG0Cr17Mn13Mo2CuN		1100	223 - 248

 

 

2. Utulivu

Chuma cha pua cha Austenitic kina upinzani bora wa kutu baada ya matibabu ya suluhisho. Hata hivyo, utupaji unapopashwa upya hadi 500°C-850°C au utupaji ukifanya kazi katika safu hii ya halijoto, CARBIDE ya chromium itashuka tena kwenye mpaka wa nafaka za austenite, na kusababisha ulikaji wa mpaka wa nafaka au kupasuka kwa weld. Jambo hili linaitwa uhamasishaji. Ili kuboresha upinzani wa kutu wa kati ya punjepunje wa kutupwa kwa chuma cha pua austenitic, kwa ujumla ni muhimu kuongeza vipengele vya aloyi kama vile titani na niobium. Baada ya matibabu ya suluhisho, joto tena hadi 850 ° C - 930 ° C, na kisha baridi haraka. Kwa njia hii, kabuidi za titani na niobiamu hutupwa kwanza kutoka kwa austenite, na hivyo kuzuia unyevu wa CARbudi ya chromium na kuboresha upinzani wa kutu wa mpaka wa nafaka wa chuma cha pua.